论文总字数：19063字

摘 要

UV减粘胶在很多领域都有很大的发展前景，但是目前国内研究进展远远落后于国外，而随着国内高新技术产业的发展，对这种减粘胶的需求会大大提高，单纯依靠进口是国内高新半导体产业发展的一大阻碍。此外，目前市场的UV减粘胶多是溶剂型，近年来环保对胶黏剂产业的要求越来越大严格，传统的溶剂型胶黏剂发展受限，而水性胶黏剂具有溶剂型胶黏剂不具备的许多优点，比如成本比较低、使用很安全、不易燃烧、污染小等。因此，开发易剥离、剥离后没有残胶、制备方法简单、且成本低的减粘胶是很有必要的。本文以羧基丁腈乳液UV减粘胶为研究对象，针对其粘结与脱粘行为进行了深入研究。

本课题主要研究内容包括：影响UV减粘胶各项性能的邻苯二甲酸二丙烯酯(DAP单体)用量、交联剂用量、增粘树脂水性松香溶液的用量、制备方式等影响因素。通过流变仪FS流变测试、流 光固化后的脱粘效果进行表征测试。最终确定兼顾高粘度、高强度、脱粘速率快等特点的UV减粘胶制备方案为：邻苯二甲酸二丙烯酯（DAP单体，软弹体）固含量为30%，水性封闭性的异氰酸酯型交联剂Y-202固含量为0.2%，水性松香乳液（增粘树脂）固含量20%，光引发剂4%，加入方式：将DAP单体和增粘树脂缓慢逐滴加入胶体。

关键词：UV减粘胶 光固化 丁腈 乳液

Study on Bonding and Debonding Behavior of Carboxylic Nitrile Emulsion UV Thinner

Abstract

UV tackifiers have great development prospects in many fields, but the current domestic research progress lags far behind foreign countries. With the development of domestic high-tech industries, the demand for such tackifiers will greatly increase, relying solely on Imports are a major obstacle to the development of the domestic high-tech semiconductor industry. In addition, the UV-reducing adhesives currently on the market are mostly solvent-based. In recent years, the environmental protection requirements for the adhesive industry have become more and more stringent. The development of traditional solvent-based adhesives is limited, while water-based adhesives have solvent-based adhesives. Adhesives do not have many advantages, such as low cost, very safe to use, not easy to burn, and little pollution. Therefore, it is necessary to develop a viscosity reducing adhesive that is easy to peel, has no residual glue after peeling, has a simple preparation method, and has low cost. This article takes carboxybutyronitrile emulsion UV tackifier as the research object, and conducts an in-depth study on its bonding and debonding behavior.

The main research contents of this topic include: the amount of dipropylene phthalate (DAP monomer), the amount of crosslinking agent, the amount of water-based rosin solution of the tackifying resin, the preparation method and other influencing factors that affect the performance of UV tackifier. Characterization test was conducted by rheometer FS rheological test and debonding effect after streamer curing. The final determination of the preparation method of the UV viscosity reduction adhesive that takes into account the characteristics of high viscosity, high strength, and fast debonding rate is: dipropylene phthalate (DAP monomer, soft elastomer) solid content is 30%, water-based sealing The isocyanate type cross-linking agent Y-202 has a solid content of 0.2%, a water-based rosin emulsion (tackifying resin) with a solid content of 20%, and a photoinitiator of 4%. The method of addition: DAP monomer and tackifying resin are slowly added dropwise to the colloid.

Keywords: UV tackifier;photocuring;nitrile;emulsion

目录

摘 要 I

Abstract II

第一章 绪论 1

1.1乳液型UV减粘胶研究背景 1

1.2UV减粘胶固化概述 1

1.2.1UV固化基理 1

1.2.2 UV固化工艺优缺点 2

1.3 水性UV固化的优缺点和发展 3

1.3.1 水性UV固化工艺优缺点 3

1.3.2 水性UV减粘胶体系的发展 4

1.4 UV减粘胶的组成和影响因素 5

1.4.1UV减粘胶的组成 5

1.4.2UV减粘胶性能的影响因素 5

1.5 本论文研究的意义和内容 6

第二章 实验部分 8

2.1实验原理 8

2.2实验内容 9

2.3实验原料和实验仪器 10

2.3.1 实验原料 10

2.3.2 实验仪器 10

2.4实验流程 11

2.4.1 样品制备 11

2.4.2DAP单体含量对减粘胶性能的影响 12

2.4.3交联剂含量对减粘胶性能的影响 13

2.4.4增粘树脂含量对减粘胶性能的影响 14

第三章 结果与讨论 16

3.1 DAP单体含量对减粘胶性能的影响 16

3.2 交联剂含量对减粘胶性能的影响 18

3.3增粘树脂含量对减粘胶性能的影响 19

第四章 结论与展望 22

参考文献 23

致谢 25

第一章 绪论

1.1乳液型UV减粘胶研究背景

UV减粘胶是被紫外光照射一定时间后可以立刻剥离、脱粘的一种胶黏剂。这种减粘胶主要用在半导体行业中，比如打磨硅片、加工芯片、芯片成型后的工艺中起固化作用^[1]。UV减粘胶除了在半导体行业有重要的作用，另外在光学仪器的剥离和其他光学材料的精细加工上也是有很大的发展前景。但是国内在减粘胶领域的发展远落后于国外，而随着国内高新技术产业的发展，对这种减粘胶的需求会大大提高，单纯依靠进口是国内高新半导体产业发展的一大阻碍^[2-4]。减粘胶，而传统型的减粘胶会产生一定的污染，不符合现在的环保领域的要求，所以传统的溶剂型减粘胶发展被限制，但是水性UV减粘胶可以弥补传统型的很多缺点，例如水性减粘胶的成本比较低、使用很安全、不易燃烧、污染小等。因此，开发易剥离、剥离后没有残胶、制备方法简单、且成本低的减粘胶是很有必要的^[5,6]。

1.2UV减粘胶固化概述

1.2.1UV固化基理

紫外光固化基本原理是在胶体中加入光引发剂混合，用高强度紫外灯照射一段时间，光引发剂将产生自由基，然后和配方中的交联剂共同作用，使配方中单体的不饱和双键和聚合物发生反应，发生交联，形成网状结构，最终形成固化，从而达到脱粘剥离的效果^[7-9]。

自由基UV光固化机理属于自由基的连锁聚合，强紫外光照射胶体，胶体产生自由基，然后自由基与体系中的稀释剂发生链增长、单体聚合、交联等反应，最终发生偶合或歧化反应终止链增长。典型反应如下图 ^[9-12]：

请支付后下载全文，论文总字数：19063字