论文总字数：13972字

摘 要

荧光颜料在纺织、油墨、安全标记、塑料产品、皮革涂饰、美化等方面已经普遍使用。但是其在使用过程中不可避免接触到水、溶剂类物质，会发生渗色 、颜色不均等不良的现象。荧光颜料在使用的过程中，容易发生溶胀从而导致渗色、颜色不均。所以，对荧光颜料在耐溶剂、耐水、耐光、耐热性等性能方面提出更高的要求。

本文先合成三聚氰胺-甲醛-苯代三聚氰胺-尿素四元共聚物作为载体树脂，然后把载体树脂和荧光染料一起进行乳化反应。最后，在催化剂的作用下，进行固化处理制备出荧光颜料。

本文主要探讨了密胺树脂组分、功能组分，以及苯代三聚氰胺的用量对荧光颜料性能的影响、反应pH值对羟甲基化的影响、反应pH值对预聚体固化的影响、反应温度的影响、荧光染料的用量对荧光强度的影响。研究表明：苯代三聚氰胺用量为2%时，荧光颜料的耐水性能和耐溶剂性能最佳；pH=8.5时，羟甲基化所需要的时间最短，产品粘度适中；反应温度为95℃；固化反应的pH值为5～5.5；染料用量为1.5%时，荧光颜料的荧光强度最强。

关键词：高性能 密胺树脂 苯代三聚氰胺 荧光颜料

Preparation of high-performance melamine resin-based fluorescent pigments powder

Abstract

Fluorescent pigments have been widely used in textile, ink, safety marking, plastic products, leather finishing, and beautification. However, it will inevitably come into contact with water and solvents in the course of use, which will lead to color change and uneven color. Fluorescence pigment in the use of the process, easy to occur swelling resulting in infiltration, color imbalance. Therefore, the fluorescence pigment in solvent resistance, water resistance, light resistance, heat resistance and other properties of higher requirements.

In this paper, melamine - formaldehyde - benzene - melamine - urea - tetrahydride copolymer was synthesized as carrier resin, then the carrier resin and fluorescent dye were emulsified together. Finally, the fluorescent pigment was prepared by curing under the action of catalyst.

This paper mainly discusses the melamine resin composition, functional components, and benzene melamine dosage effect on the properties of fluorescent pigments, reaction pH effects on hydroxyl methylation, reaction pH value on the pre polymers curing, the influence of reaction temperature, and the influence of the dosage of the fluorescent dye influence on fluorescence intensity. The results show that the water resistance and solvent resistance of fluorescent pigments are best when the dosage of benzene melamine is 2%. When pH=8.5, hydroxymethylation takes the shortest time and the product viscosity is moderate. Reaction temperature is 95 ℃. The pH value of curing reaction is 5 ~ 5.5. When the dye dosage is 1.5%, the fluorescence intensity of fluorescent pigments is the strongest.

Key words: high performance melamine resin benzene melamine fluorescent pigment

目录

摘要

Abstract

第一章 文献综述

1.1颜料

1.1.1颜料的性质 1

1.1.2有机颜料的发展史 1

1.1.3颜料的分类 2

1.1.4颜料的应用 2

1.2荧光颜料

1.2.1荧光颜料的分类 3

1.2.2荧光颜料的发光机理 5

1.2.3荧光颜料的制备方法 6

1.2.4荧光颜料的应用 8

1.3课题研究的目的和意义

第二章 实验部分

2.1实验所用药品

2.2实验所用仪器

2.3实验原理

2.3.1密胺树脂的合成机理研究 10

2.3.2高性能密胺树脂的合成机理研究 12

2.4实验步骤

2.5测试方法

2.5.1耐溶剂性能的测试 13

2.5.2耐水性能的测试 14

2.5.3荧光强度的测试 14

第三章 结果与讨论

3.1苯代三聚氰胺的用量对产品性能的影响

3.2反应pH值对羟甲基化的影响

3.3反应pH值对固化的影响

3.4荧光染料的用量对荧光强度的影响

3.5反应温度的影响

第四章 结论与展望

4.1结论

4.2展望

参考文献

致谢

第一章 文献综述

1.1 颜料

1.1.1 颜料的性质

颜料是一种大分子的物质，这种物质中含有颜色，具有维护、装潢的作用。颜料与染料的差别在于，颜料不能在水、助剂等溶剂中溶解，它是以极小的颗粒分散存在的，颜料不能发生扩散，只能进入到纤维内部，也不能与纤维分子中的任何成分发生物理、化学反应。

1.1.2 有机颜料的发展史

请支付后下载全文，论文总字数：13972字