1. 毕业设计（论文）的内容和要求

内容： 通过简单的单一源法合成形貌均一的naxfeiii[feii(cn)6] 研究其在不同铵盐中的嵌入和脱出行为，从电极材料的容量、倍率、稳定性和阻抗等方面系统地分析电解液对该类材料的影响。

要求： 掌握单一源法合成naxfeiii[feii(cn)6]并学会制备水系极片。

掌握phenom prox扫描电镜、bruker alpha红外分析仪、netzsch sta 449 f3热重仪的使用和相应数据的分析，熟练掌握非原位xrd的测试与数据分析，掌握辰华电化学工作站和蓝电电池测试系统的使用和相应数据的分析。

2. 参考文献

[1] L. Zhou, M. Zhang, Y. Wang, Y. Zhu, L. Fu, X. Liu, Y. Wu and W. Huang, Electrochim. Acta, 2017, 232, 106-113. [2] D. W. Su, A. McDonagh, S.-Z. Qiao, et al. High-capacity aqueous potassium-ion batteries for large-scale energy storage [J]. Adv. Mater. 2017, 29: 1604007. [3] Q. Yang, W. Wang, H. Li, et al. Investigation of iron hexacyanoferrate as a high rate cathode for aqueous batteries: Sodium-ion batteries and lithium-ion batteries [J]. Electrochim. Acta 2018, 270: 96-103. [4] X. Y. Wu, Y. Luo, M. Y. Sun, et al. Low-defect Prussian blue nanocubes as high capacity and long-life cathodes for aqueous Na-ion batteries [J]. Nano Energy 2015, 13: 117-123 [5] C. D. Wessells, S. V. Peddada, M. T. McDowell, et al. The effect of insertion species on nanostructured open framework hexacyanoferrate battery electrodes [J]. J. Electrochem. Soc. 2012, 159: A98-A103. [6] M. R. Lukatskaya, O. Mashtalir, C. E. Ren, et al. Cation intercalation and high volumetric capacitance of two-dimensional titanium carbide [J]. Science 2013, 341: 1502-1505. [7] X. Y. Wu, Y. T. Qi, J. J. Hong, et al. Rocking-chair ammonium-ion battery: a highly reversible aqueous energy storage system [J]. Angew. Chem. Int. Ed. 2017, 56: 1-6. [8] X. Y. Wu, Y. K. Xu, H. Jiang, et al. NH4 topotactic insertion in Berlin green: an exceptionally long cycling cathode in aqueous ammonium-ion batteries [J]. ACS Appl. Energy Mater. 2018, 1: 3077-3083. [9] J. J. Holoubek, H. Jiang, D. Leonard, et al. Amorphous titanic acid electrode: its electrochemical storage of ammonium in a new water-in-salt electrolyte [J]. Chem. Commun. 2018, 54: 9805-9808. [10] J. F. Qian, C. Wu, Y. L. Cao, et al. Prussian blue cathode materials for sodium-ion batteries and other ion batteries [J]. Adv. Energy Mater. 2018, 8: 1702619.

3. 毕业设计（论文）进程安排

2019年1月2日~2019年2月18日 完成文献调研 2019年2月19日~2019年2月28日 整理并完成开题报告 2019年3月1日~2019年3月10日 完成电极材料及电极片的制备及其物理表征与数据分析 2019年3月11日~2019年3月31日 完成电极材料的电化学新性能测试及数据分析 2019年4月1日~2019年4月28日 对实验数据进行补充并完成毕业论文的撰写