1. 毕业设计（论文）的内容和要求

主要内容包括：采用种子乳液聚合方法合成具有不同结构的丙烯腈-丙烯酸丁酯-苯乙烯（asa）共聚物。

首先通过在聚合体系中加入不同量的交联剂（甲基丙烯酸烯丙酯）制备具有不同交联程度pba核的asa，研究pba交联程度对聚甲基丙烯酸甲酯（pmma）增韧改性影响；其次，制备具有不同粒径pba核的asa，研究pba核粒径对pmma增韧改性影响；最后改变pba与san比例，制备不同核壳比例的asa，研究不同核壳比asa对pmma的韧性影响，并提出增韧机理。

实验采用模压法制备测试样品，并借助zetapals粒度测量仪、冲击试验机、电子万能试验机、动态机械热分析（dmta）、扫描电子显微镜（sem）、傅里叶变换红外光谱仪（ftir）等，分析合成asa粒径大小、增韧改性效果、体系玻璃化转变温度、相容性及各基团间相互作用等。

2. 参考文献

[1] Ren L, Zhang M Y, Han Y, et al. Core-shell particles for design of high-performance polymeric materials with good transparency and toughness[J]. Journal of Polymer Research, 2014, 21(12):1-7. [2] Tolue S, Moghbelia M R. Preparation of ASA (acrylonitrile-styrene-acrylate) structural latexes via seeded emulsion polymerization[J]. European Polymer Journal, 2009, 45(3):714-720. [3] Xiang B, Zhang J. New insights into the impact toughness of ASA (acrylonitrile-styrene-acrylate) with controllable core#8211;shell structure synthesized by three-stage seeded emulsion polymerization[J]. International Journal of Polymer Analysis Characterization, 2017. [4] Palmer C. Seeded Semibatch Emulsion Polymerization ofn-Butyl Acrylate. Kinetics and Structural Properties[J]. Macromolecules, 2000, 33(14):5041-5047. [5] Liu Z, Han Y, Zhou C, et al. Seeded Emulsion Polymerization of Butyl Acrylate Using a Redox Initiator System: Kinetics and Mechanism[J]. Industrial Engineering Chemistry Research, 2010, 49(16):7152-7158. [6] Liu Z, Deng Y, Ye H, et al. Toughening of Polyamide-6 with a Maleic Anhydride Functionalized Acrylonitrile-Styrene-Butyl Acrylate Copolymer[J]. Industrial Engineering Chemistry Research, 2012, 51(27):9235-9240. [7] Ludivine Bouvierfontes, Rosangela Pirri, And J M A, et al. Seeded Semicontinuous Emulsion Copolymerization of Butyl Acrylate with Cross-Linkers[J]. Macromolecules, 2005, 38(4):1164-1171. [8] Vazquez F, Schneider M, Pith T, et al. Effect of the composition of structured rubber particles on the toughness of poly(methylmethacrylate)[J]. Polymer International, 2015, 41(1):1-12. [9] Song J, Kim J, Suh K. Poly(methyl methacrylate) toughening with refractive index‐controlled core#8211;shell composite particles[J]. Journal of Applied Polymer Science, 2015, 71(10):1607-1614. [10] Cho K, Yang J H, Chan E P. The effect of interfacial adhesion on toughening behaviour of rubber modified poly(methyl methacrylate)[J]. Polymer, 1997, 38(20):5161-5167. [11] Xu X, Wang R, Tan Z, et al. Effects of polybutadiene-g-SAN impact modifiers on the m ology and mechanical behaviors of ABS blends [J]. European polymer journal, 2005, 41(8): 1919-1926. [12] Ren L, Li Y, Zhang M, et al. Toughness, dynamic mechanical property, and morphology of polyvinylchloride/acrylonitrile‐styrene‐butyl acrylate blends[J]. Journal of Vinyl Additive Technology, 2016, 22(1):43-50. [13] 韩业. ASA 树脂及其共混物的制备和性能研究 [D]. 吉林: 吉林大学, 2009. [14] 武利民, 于在璋, 李伯耿, 等. ASA核-壳乳液聚合物的组成, 结构与性能[J]. 石油化工, 1992,21(1): 1-5. [15] 马令庆. ASA的制备及其改性PVC的研究[D]. 青岛科技大学, 2012. [16] 曹同玉, 刘庆普, 胡金生. 聚合物乳液合成原理性能及应用[M]. 化学工业出版社, 1997. [17] 伍雪强. 有机玻璃的增韧改性研究[D]. 苏州大学, 2009.

3. 毕业设计（论文）进程安排

起讫日期 设计（论文）各阶段工作内容 备 注 2.26-3.11 文献查询及文献翻译 3.12-3.18 完成开题报告 3.19-4.22 实验工作 4.23-4.29 论文中期检查 4.30-6.10 进行实验并撰写论文 6.11-6.22 论文答辩