论文总字数：19716字

摘 要

随着我国工业等各方面的迅速发展，每年排放的大量工业副产石膏成为了一个不可忽视的问题。存放这些工业上产生的废弃物不仅会浪费土地资源而且会污染环境和地下水资源。从工业废料的二次利用、能源节约和“以人为本”的方面考虑，本文提出以建筑石膏为主要原料，通过添加不同的轻质骨料并掺入一些助剂来提高其性能，制作用于地面保温的性能良好的石膏基砂浆。用控制变量的方法，分别研究了玻化微珠和陶粒作为砂浆保温颗粒以及助剂掺量不同时，对保温砂浆干密度、抗压强度、导热系数等性能的影响，并确定了用于地面保温的砂浆的各种组分的合理配比。

本文通过试验，得出了以下一些结论：（1）为使砂浆达到建筑施工的要求，缓凝剂选择石膏专用缓凝剂（SG-10），且其掺量为0.3%；减水剂的掺量为0.7%。（2）用玻化微珠和陶粒分别作为砂浆保温颗粒时，都能降低砂浆的导热系数，虽然砂浆的抗压强度有所下降，但其绝干密度变小，且保温性能也随着保温颗粒含量的变多而变好。玻化微珠作为保温颗粒时，砂浆的绝干密度不仅更小，而且保温效果也比陶粒的效果好，所以，为制备各方面性能都更好的轻质石膏材料，玻化微珠相对于陶粒更加适合作为石膏基砂浆的保温颗粒。（3）保水剂含量的增多，砂浆的导热系数变小，但其抗压强度和干密度都会有明显的减弱。（4）随着可分散乳胶粉含量的增加，保温砂浆的干密度有所下降，这是因为胶粉引入了空气的原因。胶粉的含量较小时，因为其在搅拌的时候引入的气泡的量较少，所以保温砂浆抗压强度减小得较少；但当胶粉的掺量继续增加时，其抗压强度减小得就较为多了，所以胶粉的掺量不适宜过大。这是由于如果胶粉的含量过多，它就会引入大量的气泡，从而降低了砂浆的抗压强度。

关键词：保温砂浆 建筑节能 环境保护 干密度 抗压强度 导热系数

Preparation and properties of gypsum-based thermal insulation

Abstract

With the rapid development of China's industry and other aspects of a large number of industrial by-product gypsum, annual emissions became a problem that can not be ignored. Store these solid wastes not only occupy a lot of land and pollute the environment and groundwater resources. From the resource utilization of industrial waste gypsum, building energy efficiency as well as and"people-oriented" point of view, this paper presents with an industrial by-product gypsum as the main raw material, by adding different lightweight aggregate and incorporated some of the aid to improve its performance, productgypsum-based mortar for ground insulation with good performance. Variable control methods were investigated as ceramic and glass beads of insulation mortar lightweight aggregate and additive content is not the same effect on the thermal insulation properties, and various groups are used to determine the thermal insulation of the ground reasonable proportion points. Finally, this paper also discussed the development of thermal insulation mortar and gypsum-based applications.

Through experiments, some experimental results were obtained, reached the following conclusions: (1) In order to meet the requirements of construction of mortar, plaster retarder select special retarder (SG-10), and its content is 0.3%; superplasticizer dosage is 0.7%. (2) With ceramic and glass beads were used as insulation particles mortar, mortar can improve it’s performance, although the compressive strength of mortar has declined, but it becomes less dense bone dry, and the insulation performance with insulation increase, the particle content is better. Glass beads used as insulation particles, the density of dry mortar must not only smaller, but the insulation effect is better than ceramic effect, so, to prepare performance superior lightweight gypsum-based insulation materials, glass beads is more suitable than Tao Reap as a mortar insulation particles. (3) An increase in the content of water-retaining agent, will improve thermal properties of the mortar, but its compressive strength and dry density are significantly weakened. (4) With the incorporation of polymer powders, thermal insulation mortar dry density decreased, which is related to polymer powders bleed air. When the powder content is small, due to the relatively small amount of its introduction in the mixing of air bubbles, reduce the compressive strength of mortar was less; but when powder content continues to increase, the compressive strength was reduced to more and more, so the powder dosage should not be too large. This is because of the excessive doping, the introduction of excessive amount of bubbles, weakened mortar compressive strength.

KeyWords:Thermal insulation mortar; building energy conservation; environmental protection; dry density; compressive strength; thermal conductivity

目 录

摘要 I

Abstract II

第一章 绪论 1

1.1 课题研究背景及意义 1

1.2 保温砂浆的研究状况及发展趋势 1

1.2.1 保温砂浆的种类及特点 1

1.2.2 保温砂浆的研究现状 1

1.2.3 保温砂浆的发展趋势 2

1.3石膏基保温砂浆的组成 2

1.4本文主要研究工作 5

第二章 试验材料及试验方法 7

2.1 试验材料 7

2.1.1 建筑石膏 7

2.1.2 填料 7

2.1.3 保温颗粒 8

2.1.4 外加剂 8

2.2 试验所用仪器 8

2.3 试验方法 9

2.3.1干密度的测定 9

2.3.2 抗压强度的测定 9

2.3.3导热系数的测定 10

第三章 石膏基保温砂浆的制备与研究 11

3.1缓凝剂对建筑石膏性能的影响 11

3.2减水剂对建筑石膏性能的影响 13

3.3 保温颗粒对砂浆性能的影响 15

3.4纤维素醚对砂浆性能的影响 17

3.5 可再分散乳胶粉对砂浆性能的影响 19

第四章 结论 22

参 考 文 献 23

致谢 25

第一章 绪论

1.1 课题研究背景及意义

人类生存和发展必须依赖能源，我国是人口众多的国家，能源消耗会比较严重，而能源消耗中的建筑能耗在这些总能耗中所占比重越来越大，如何将建筑能耗降低，实现建筑节能，在国内的资源和能源越来越少的窘迫下变得尤其重要。所谓的建筑能耗主要指生活和工作中的用电以及对建筑房屋的质量的改变等方面。现阶段，我国的建筑节能主要是针对墙体、屋面等围护结构，而对于占有建筑结构很大比例的楼地面研究很少，将主要应用于墙体的保温砂浆应用于地面保温，且将普通保温砂浆结合自流平材料，开发出一种具有一定流动性能的地面保温材料具有重要的意义^[1]。

1.2 保温砂浆的研究状况及发展趋势

1.2.1 保温砂浆的种类及特点

保温砂浆使用一些具有良好的热绝缘特性的材料作为轻质骨料、石膏为胶凝材料，并按一定的比例加入添加剂制得的^[2]。保温砂浆按化学成分可分为有机和无机两大类。然而，不管是无机保温砂浆还是有机保温砂浆，都有一些不可避免的缺点。比如无机保温砂浆的性能是热性能稍差、强度低、抗开裂性差、工作效率低下，所以广泛地在建筑工业中应用无机保温砂浆受到了极大的限制。而且，目前我们在土木工程和工程建设中使用的有机保温砂浆，虽然具有优异的保温效果，但也有缺点，如他们的耐火性差、耐候性差、容易老化、机械性能差、易开裂、寿命短。因此，要使保温砂浆能够使用更长的时间，增强物理和机械性能，是目前保温砂浆要解决的问题^[3]。

1.2.2 保温砂浆的研究现状

尽管保温砂浆存在着一些缺点，但近年来，通过一些学者的研究，保温砂浆的性能已经提升了很多。为了满足各种不同的需求，许多新型保温砂浆被开发了出来。例如：重庆大学的陈明凤，彭家惠等人就利用聚苯乙烯泡沫、水泥和膨胀珍珠岩等研究出了一种可用于建筑物外墙保温的砂浆，该砂浆不仅具有良好的抗裂性能而且耐候性也比一般的保温砂浆优异。杨俊晓等人又用粒化高炉矿渣替代砂研制出了一种具有高强度且密度和导热系数都较小的砂浆，该砂浆可用于保温砌筑。Bulent Yesilata等人用废弃的PET和橡胶加入到混凝土中来提高墙体的保温性能，这提高了垃圾的回收利用率，对环境保护具有非常重要的意义^[4]。

1.2.3 保温砂浆的发展趋势

随着科技的不断进步，各种新型产品层出不穷，保温砂浆的种类和性能也迅速发展，产品日益丰富。研制出的新型保温砂浆能很好地解决建筑材料在生产和应用过程中资源、能源和环境三方面协调发展的问题，具备了高性能和绿色化的优点。这些也都将是保温砂浆未来的发展可能性，大致的发展方向为：

（1）高性能