论文总字数：26106字

摘 要

本文对面层粉刷石膏和底层粉刷石膏进行了研究，底层研究了在使用了25%的脱硫灰取代脱硫石膏制备石膏砂浆时，选取三聚磷酸钠、葡萄糖酸钠、柠檬酸钠、蛋白类（SG-10）这四种缓凝剂通过单掺及复配测定对掺有脱硫灰的脱硫石膏初凝时间、终凝时间、抗压强度和抗折强度等宏观性能的影响。实验结果表明，从缓凝效果来看，在含有亚硫酸钙的体系中，缓凝剂单掺时，缓凝效果葡萄糖酸钠gt;柠檬酸钠≥蛋白类gt;三聚磷酸钠。从强度来看，葡萄糖酸钠、柠檬酸钠、SG-10这三种缓凝剂都对强度有负作用，特别是SG-10掺量越大，强度损失越大，当掺量到1.5‰时，抗压强度损失达到28%；三聚磷酸钠能够增强石膏砂浆强度，但是掺量不能多大，掺量过大又不利于石膏砂浆的强度发展，最佳掺量建议在1‰；面层研究了不同掺量的高强石膏、水泥和有机硅对粉刷石膏的溶蚀率、强度和软化系数的影响对面层粉刷石膏耐水性能的影响进行了研究。实验结果表明，外掺高强石膏、水泥和有机硅都能提高面层粉刷石膏的耐水性能，高强石膏主要是通过降低石膏的溶蚀率，提高石膏的抗压强度和提高石膏的软化系数来实现的，水泥则是通过降低石膏的溶蚀率和提高是高的抗压强度来实现的，有机硅则是通过提高石膏的软化系数来实现的。并且水泥对溶蚀率的影响最为显著，有机硅对软化系数的影响最显著。

关键词 粉刷石膏 缓凝剂 耐水

ABSTRACT

In this paper, the FGD gypsum plaster and the FGD gypsum for base coating are studied.Researching the preparation of gypsum mortar instead of desulfurization gypsum desulfurization ash used 25%, selection of sodium tripolyphosphate, sodium gluconate, sodium citrate, proteins (SG-10) of these four kinds of retarder of desulfurization gypsum desulfurization ash of initial setting time, final setting time,compressive strength and flexural strength of macro properties of the doped were determined by single doped and compound. The experimental results show that, the retarding effect, in the presence of calcium sulfite system, retarder single doped, retarding effect of sodium gluconate gt; sodium citrate ≥ proteingt;sodium tripolyphosphate. From the strength point of view, sodium gluconate, sodium citrate, SG-10 these three kinds of Retarder on the intensity of negative effect, especially the SG-10 content is greater, the greater the loss of strength, when the dosage to 1.5 ‰, compressive strength loss reached 28%;sodium tripolyphosphate can enhance the strength of gypsum mortar, but content not much, amount of strength development is not conducive to the gypsum mortar, the best dosage suggestions in 1 ‰. The surface layer of the different content of high-strength gypsum, cement and gypsum silicone on the corrosion rate, strength and softening coefficient of gypsum waterproof paint across the layer properties were studied. The experimental results show that, with high strength gypsum, cement and silicone can improve the water resistance of the surface layer of gypsum plaster, gypsum plaster is mainly by reducing the corrosion rate, improve the compressive strength of gypsum plaster and improve the softening coefficient of cement is realized, by reducing the corrosion rate and improve the gypsum is compressive strength high to achieve, silicone is by improving the softening coefficient of gypsum. And cement influence on corrosion rate is the most significant, the most significant effect on the softening coefficient of silicone.

Keywords: FGD gypsum plaster；Retarder;water-tolerant

目 录

摘要 I

ABSTRACT II

第1章 绪论 1

1.1 脱硫石膏 1

1.1.1 脱硫石膏概述 1

1.1.2 脱硫石膏的物化性能 1

1.1.3 脱硫石膏的应用情况 2

1.2 粉刷石膏 4

1.2.1 粉刷石膏概述 4

1.2.2 粉刷石膏的特性 5

1.2.3 粉刷石膏的研究状况 6

1.2.4粉刷石膏防水 8

1.3本课题研究的内容 9

1.4本课题研究目的及意义 9

第二章 原材料及试验方法 10

2.1 原材料 10

2.1.1 脱硫建筑石膏 10

2.1.2高强石膏 10

2.1.3 重钙粉 11

2.1.4水泥 11

2.1.5 有机硅 11

2.1.6 外加剂 11

2.2 试验方法 11

2.2.1 建筑石膏标准稠度用水量的测定 11

2.2.2 建筑石膏凝结时间的测定 11

2.2.3 建筑石膏抗折、抗压强度的测定 12

2.2.4 粉刷石膏标准扩散度用水量的测定 12

2.2.5 粉刷石膏凝结时间的测定 12

2.2.6 粉刷石膏强度的测定 12

2.2.7 溶蚀率的测定 13

2.2.8软化系数的测定 13

第三章 不同种缓凝剂对含有脱硫灰的石膏砂浆的性能影响 14

3.1 缓凝剂对石膏砂浆凝结时间的影响 14

3.2 缓凝剂对石膏砂浆强度的影响 16

3.3缓凝剂对石膏形貌影响 17

3.3.1柠檬酸钠掺量对脱硫石膏晶体形貌的影响 17

3.3.2缓凝剂种类对脱硫石膏晶体形貌的影响 18

3.4缓凝剂对石膏砂浆孔隙率的影响 19

3.5 本章小结 20

第四章 面层粉刷石膏耐水性研究 21

4.1防水组分对面层石膏溶蚀率的影响 21

4.2防水组分对面层石膏抗压强度的影响 23

4.3防水组分对面层石膏软化系数的影响 25

4.4本章小结 27

第五章结论和展望 28

5.1结论 28

5.2 展望 28

参考文献 29

致谢 30

第1章 绪论

1.1 脱硫石膏

1.1.1 脱硫石膏概述

我国目前生产电力主要以燃煤发电为主，因此需要大量燃烧煤炭，由于中国的煤炭含硫量大，灰分高，我国煤炭燃烧形成的大量SO₂会形成酸雨恶化环境给我国造成巨大的经济损失。

脱硫石膏（Flue Gas Desulphurization Gypsum），简称FGD石膏，又称烟气脱硫石膏或硫石膏，是烟气进行脱硫净化处理后的主要副产物^[1]。随着人们对环境保护的呼声和国家对环境保护的要求不断加强，必须要加强燃煤脱硫工作。烟气脱硫是目前电厂控制SO₂排放最成熟和最有效的方法，烟气脱硫可以分为湿法脱硫、半干法脱硫和干法脱硫三大类。其中应用最广泛的是湿法脱硫。脱硫石膏的形成过程如下^[2]：

请支付后下载全文，论文总字数：26106字