论文总字数：18531字

摘 要

聚烯烃（PO）材料由于其各个方面的性能都比较优良、来源广泛、价格便宜等优点被广泛应用于各个领域。但是PO在燃烧时的燃烧速度非常快，并且伴有烟尘、熔融滴落等现象，所以PO在被应用的时候必须进行阻燃改性。而在卤系阻燃剂和无卤的阻燃剂之间，由于所谓的对环境和人体健康的危害，人们更愿意去使用无卤的阻燃剂。但是许多研究都表明了无卤阻燃剂还存在着很多的问题，无卤阻燃剂还无法完全取代卤系阻燃剂。盲目使用无卤阻燃剂会带来很大的风险，无卤阻燃剂还需要更多的改进。其次，阻燃剂与其他化学物质一样，阻燃剂的是否环保并非是由它是否含有卤素原子决定，而是由阻燃剂的具体化学结构决定的，这也是本次课题选择卤系阻燃剂的原因之一。但是如果直接使用阻燃剂对PO进行阻燃改性，阻燃剂很容易在材料中分布含量参差不齐，为了保证阻燃的效果，就需要加入大量的阻燃剂，阻燃剂的含量高了就会影响材料性能。因此，现在市场上主要采用母粒的方式对PO进行改性。本课题主要研究的是添加不同组分的含卤阻燃母粒的PO在不同性能上的表现区别，并探索出在实际应用中阻燃母粒的最佳添加量。

关键词： PO 阻燃 母粒

Application and research of flame retardant masterbatch in polyolefin

Abstract

Polyolefin(PO) material has been widely used in all kinds fields because of its excellent performance,wide sources and low price.However the burning speed of PO is very fast, accompanied by soot,melting and dripping and other phenomenon,so the flame retardant modification of PO must be carried out when it is applied.Between halogen flame retardants and halogen-free flame retardants,people are more willing to use halogen-free flame retardants because of the so called harm to the environment and human health.However,many studies have shown that halogen-free flame retardants still have many problems,and halogen-free flame retardants cannot completely replace halogen flame retardants.The blind use of halogen-free flame retardants is very dangerous,halogen-free flame retardants still need more study.Secondly,like other chemical substances,the environment protection of flame retardants is not determined by whether they contain halogen atoms,but by the specific chemical construction of the flame retardants,which is also one of the reasons for choosing halogen flame retardants in this study.However,if PO are flame retardant modified directly by flame retardants,the content of flame retardants in the material is very easy becoming irregularity.In order to ensure the flame retardant effect,a large number of flame retardants need to be added.A high content of flame retardants will affect the material properties.Therefore,the main way to modify PO in the market is using masterbatch.This subject mainly studies the differences in the performance of PO containing halogen flame retardants masterbatches with different components,and explores the optimum additive quantity of flame retardant masterbatches in practical applications.

Keywords: PO Flame retardant Masterbatch

目录

摘 要 I

ABSTRACT II

第一章 前 言 1

1.1课题背景 1

1.2本课题工作 1

第二章 理论部分 2

2.1聚丙烯 2

2.1.1简介 2

2.1.2结构与性能 2

2.1.3生产工艺 2

2.1.4燃烧机理 3

2.1.5阻燃机理 3

2.2聚乙烯 4

2.2.1简介 4

2.2.2结构与性能 4

2.2.3生产工艺 5

2.2.4燃烧机理 6

2.2.5阻燃机理 6

2.3阻燃剂 7

2.3.1简介 7

2.3.2阻燃剂的分类 7

2.4母粒 9

2.4.1简介 9

2.4.2阻燃母粒的制备 10

2.4.3阻燃剂的选择 10

2.4.4载体的选择 10

2.4.5助剂的选择 11

2.4.6母粒的加工工艺与使用 11

第三章 实验部分 12

3.1样品的制备 12

3.2氧指数法 12

3.3UL94垂直燃烧实验 14

3.4力学性能的测试 14

3.5X射线衍射分析（XRD） 14

3.6 扫描电子显微镜分析（SEM） 15

3.7差示扫描量热法（DSC） 17

第四章 未来与展望 19

参考文献 20

致谢 23

请支付后下载全文，论文总字数：18531字