1. 毕业设计（论文）的内容和要求

白色发光二极管(白光led)作为一种新型的固态照明器件以其高光效、低能耗、长寿命及环境友好等特点已在平板显示背光源、汽车前灯、道路照明等领域获得了初步应用。

目前白光led获得白光发射最有效的途径仍是基于蓝光(~460 nm)或近紫外光(~390 nm)的荧光粉转换法，其工艺简单、成本低，占据市场主导地位。

但目前商用红粉面临着化学稳定性差(猝灭温度低)、色纯度与发光效率低等问题，特别是适用于近紫外芯片的红粉，其发光强度不足蓝粉与绿粉的八分之一。

2. 参考文献

[1]S. Ye, F. Xiao, Y. X. Pan, Y. Y. Ma, Q. Y. Zhang, Mater. Sci. Eng. 71, 1-34 (2010) [2]Y.Y. Tsai, H.R. Shih, M.T. Tsai, Y.S. Chang, Mater. Chem. and Phys. 143, 611-615 (2014) [3]D.Q. Zhang, Y.F. Liu, Y.N. Lu, H. Chen, F.L. Yang, H.M. Wu, J. Mater. Sci. Mater. Electron. 25, 2359-2365 (2014) [4]H. Amano, N. Sawaki, I. Akasaki, Y. Toyoda, Appl. Phys. Lett. 48, 353 (1986) [5]T.C. Ozawa, K. Fukuda, K. Akatsuka, Y. Ebina, T. Sasaki, K. Kurashima, K. Kosuda, J. Phys. Chem. C. 112, 17115-17120 (2008) [6]X.G. Xi, P.Y. Dong, L.L. Han, R.F. Guan, G.H. Hou, J. Lumin. 159, 280-283 (2015) [7]Z. Lu, L. Zhang, N.C. Xu, L.X. Wang, Q.T. Zhang, Spectrosc. Spect. Anal. 32, 2632-2636 (2012) [8]J.S. Hou, X. Yin, F.Q. Huang, W.Z. Jiang, Mater. Res. Bull. 47, 1295-1300 (2012) [9]L. Zhang, Q. Liu, N. Ding, H. Yang, J. Zhang, Q.T Zhang, Sci. Adv. Mater. 7, 1-10 (2015) [10]K. V. Dabre, K. Park and S. J. Dhoble, Synthesis, J. Alloy. Compd. 617, 129-134 (2014) [11]L. Zhang, P.D. Han, Y. Han, Z. Lu, H. Yang, L.X. Wang, Q.T. Zhang, J. Alloy. Compd. 558, 229-235 (2013) [12]H.Y. Li, H.K. Yang, J.H. Jeong, K. Jang, H.S. Lee, S.S. Yi, Mater. Res. Bull. 46, 1352-1358 (2011) [13]X. Yin, J.Y. Yao, Y.M. Wang, C.C. Zhao, F.Q. Huang, J. Lumin. 132, 1701-1704 (2012) [14]Z. Lu, L. Zhang, L.X. Wang, Q.T. Zhang, J. Nanomater. 2012, 1-7 (2012) [15]J.A. Wani, N.S. Dhoble, N.S. Kokode, B.D. Raju, S.J. Dhoble, J. Lumin. 147, 223-228 (2014) [16]M. Ferhi, C. Bouzidi, K. Horchani-Naifer, H. Elhouichet, M. Ferid, J. Lumin. 157, 21-27 (2015) [17]S. Ye, C.H. Wang, Z.S. Liu, J. Lu, X.P. Jing, Appl. Phys. B. 91, 551-557 (2008) [18]S. Ye, C.H. Wang, X.P. Jing, J. Electrochem. Soc. 155, J148-J151 (2008) [19]H.D. Nguyen, S.J. Kim, I.H. Yeo, S. Mho, J. Electrochem. Soc. 159, J54-J60 (2012) [20]L. Zhang, Z. Lu, P.D. Han, L.X. Wang, Q.T. Zhang, J. Mater. Chem. C. 1, 54-57 (2013) [21]G. King, L.M. Wayman, P.M. Woodward, J. Solid State Chem. 182, 1319-1325 (2009) [22]M.C. Knapp, P.M. Woodward, J. Solid State Chem. 179, 1076-1085 (2006) [23]W.M. Yang, L.X. Wang, X.C. Lu, Q.T. Zhang, J. Mater. Sci. Mater. Electron. 26, 1113-1118 (2015) [24]X Yin, Y.M. Wang, F.Q. Huang, Y.J. Xia, D.Y. Wan, J.Y. Yao, J. Solid State Chem. 184, 3324-3328 (2011) [25]V. Sivakumar, U.V. Varadaraju, Electrochem. Solid St. 9, H35-H38 (2006)

3. 毕业设计（论文）进程安排

起讫日期 设计（论文）各阶段工作内容 备 注 12月17号到 12月31号 查阅国内外相关文献 1月4号到 1月15号 掌握溶胶凝胶法制备钨酸盐玻璃的工艺方法 1月15号到 2月28号 放寒假 3月1号到 3月25号 掺杂不同浓度的Eu3 ，确定最佳掺杂浓度 3月26号到 4月30号 制备不同浓度Li 、Gd 掺杂的NaLaMgWO6:Eu3 粉体，讨论掺杂量对其结构变化的影响 5月1号到 5月7号 放假 5月8号到 5月31号 使用相关软件处理分析实验数据，结合理论知识总结实验结果 6月1号到 6月15号 写毕业论文，准备答辩