论文总字数：15627字

摘 要

水性环氧树脂是指环氧树脂以微粒或液滴的形式分散在以水为连续相的分散介质中而配得的稳定分散体系。由于环氧树脂是线型结构的热固性树脂，所以施工前必须加入水性环氧固化剂，在室温环境下发生化学交联反应，环氧树脂固化后就改变了原来可溶可熔的性质而变成不溶不熔的空间网状结构，显示出优异的性能。水性环氧树脂涂料除了具有溶剂型环氧树脂涂料的诸多优点：

一是适应能力强，对众多底材具有极高的附着力，固化后的涂膜耐腐蚀性和耐化学药品性能优异，并且涂膜收缩小、硬度高、耐磨性好、电气绝缘性能优异等；

二是环保性能好，还具有不含有机溶剂或挥发性有机化合物含量较低，不会造成空气污染，因而满足当前环境保护的要求；

三是真正水性化，以水作为分散介质，价格低廉、无气味、不燃，储存、运输和使用过程中的安全性也大为提高；

四是操作性佳，水性环氧树脂涂料的施工操作性能好，施工工具可用水直接清洗，可在室温和潮湿的环境中固化，有合理的固化时间，并保证有很高的交联密度。这是通常的水性丙烯酸涂料和水性聚氨酯涂料所无法比拟的。水性环氧树脂以其突出的性能优势，使制备得到的水性环氧树脂涂料同样具有优异的性能，从而在水性产品大家族里地位越来越重要，专家认为水性环氧树脂在环保化的今天，前景十分开阔。

关键词：环氧树脂, 酯化反应, 环氧丙烯酸酯, 水性

Synthesis of waterborne epoxy acrylic resin terpene

Abstract

Waterborne epoxy resin refers to an epoxy resin in the form of particles or droplets dispersed in water as the continuous phase of the dispersion medium and worthy of a stable dispersion. Since the epoxy resin is a thermosetting resin linear structure, it must be added before the construction of waterborne epoxy curing agents, chemical cross-linking reaction occurs at room temperature, epoxy curing after changing the original nature of novolac becomes into insoluble and infusible spatial network structure, it exhibits excellent properties. Waterborne epoxy resin coatings have many merits like solvent type epoxy resin coating：

One is adaptable for numerous substrates with high adhesion and excellent corrosion resistance coating after curing and chemical resistance, and the film shrinkage, high hardness, wear resistance, and excellent electrical insulation properties and so on;

Second, environmental performance, but also has no organic solvent or low levels of volatile organic compounds will not cause air pollution, and thus meet current environmental protection requirements;

Third, the real water-based, with water as a dispersion medium, low prices, odorless, non-flammable, storage, transport and use of security has been greatly improved;

Fourth, good operability, the construction operation of waterborne epoxy coating is good, construction tools can not use water to clean, can

be cured at room temperature and humid environment, there is a reasonable curing time, and to ensure a high crosslink density. This is a common water-based acrylic paints and water-based polyurethane coatings unmatched. Waterborne epoxy resin for its outstanding performance advantages, so prepared aqueous epoxy coating also has excellent performance, resulting in a large family of water-based products in an increasingly important position, experts believe waterborne epoxy resin in environmental protection today the prospects are very broad.

Keywords: epoxy resin, esterification, epoxy acrylate, waterborne

目录

摘要 I

Abstract II

第一章 文献综述 1

1.1 环氧树脂概述 1

1.2 萜烯及其衍生物 1

1.3 水性环氧树脂的合成 2

1.3.1 机械法 2

1.3.2 化学改性法 2

1.3.3 相反转法 4

1.3.4 固化剂乳化法 4

1.4 水性环氧树脂的优点 4

第二章 水性环氧丙烯酸酯的制备与表征 6

2.1 前言 6

2.2 实验部分 6

2.2.1 主要原材料 6

2.2.2 实验方法 7

2.2.3 表征 8

2.2.4 萜烯基的引入 8

2.3 结果与讨论 10

2.3.1 各种参数的测定 10

2.3.2 反应温度对聚合反应速度及双键含量的影响 12

2.3.3 反应时间对酸值和粘度的影响 14

2.3.4 催化剂用量对反应速率的影响 15

2.3.5 阻聚剂用量对实验的影响 16

第三章 结论 18

参考文献 19

致谢 20

第一章 文献综述

1.1 环氧树脂概述

环氧丙烯酸酯树脂又称乙烯基酯树脂，是环氧树脂和丙烯酸进行反应后溶解于苯乙烯中的变性环氧树脂。

环氧丙烯酸酯树脂具有环氧树脂的优良特性，但是固化性和成型性方面更为出色，不象环氧树脂那样烦琐，是一种热固化性树脂。它具有优异的耐水性、耐热水性、耐药物性、粘结性、韧性^[1]。通过有机过氧化物固化法（低温-高温）或光固化法便能进行固化，被广泛应用于以下领域：耐腐蚀FRP制品，如玻璃钢槽罐、管道、塔器以及耐腐蚀格栅等；防腐蚀工程，如水泥基或铁基玻璃钢衬里、高耐腐蚀地坪；高强度FRP，例如拉挤玻璃钢型材、体育用品、FRP船艇等；重防腐玻璃鳞片涂料；其他如UV油墨、重防腐工业地坪等。

请支付后下载全文，论文总字数：15627字