论文总字数：16212字

摘 要

本文以ESA/TPEO/AMPS为单体聚合形成新型三元阻垢剂，与目前市面上常见的PBTCA进行复配，形成一种新型二元复配阻垢剂。运用静态阻垢法，控制变量，对其阻硫酸钙垢性能进行研究。研究了单体配比不同，反应温度不同，反应时间不同，钙离子浓度不同对阻垢性能的影响。研究发现对于m(ESA):m(TPEO):m（AMPS）=1:1:5与PBTCA按照体积比1:1复配的二元阻垢剂，在钙离子浓度一定的情况下，70℃下保温6小时的阻垢率最佳，最高可以达到86.17%。使用红外光谱（FTIR）以及高倍显微镜和扫描电镜对加入阻垢剂前后析出的硫酸钙垢进行分析，通过对其样貌的观察可以得出硫酸钙垢的晶体晶型发生了变化，阻垢剂会对晶体生长有阻碍作用。新型三元聚合物（ESA/TPEO/AMPS）与PBTCA的复配产物合成工艺简单，阻垢性能良好，适用范围广，价格廉价，其中的含磷含氮量小，对环境友好，是一种优良的新型绿色环保阻垢剂。

关键词： 水处理剂；绿色环保；二元复配；阻硫酸钙

Study on the performance of a new type of polyether-containing terpolymer compound product to inhibit calcium sulfate

Abstract

In this paper, ESA/TPEO/AMPS is used as monomers to polymerize to form a new type of ternary scale inhibitor, which is compounded with the current common PBTCA on the market to form a new type of binary compound scale inhibitor. The static scale inhibition method was used to control the variables, and the calcium sulfate scale inhibition performance was studied. The effects of different monomer ratios, different reaction temperatures, different reaction times, and different calcium ion concentrations on the scale inhibition performance were studied. The study found that for the binary scale inhibitor compounded with m(ESA):m(TPEO):m(AMPS)=1:1:5 and PBTCA in a volume ratio of 1:1, at a certain calcium ion concentration, 70 The anti-scaling rate of 6 hours at ℃ is the best, and the highest can reach 86.17%. Using infrared spectroscopy (FTIR) and high magnification microscope to analyze the calcium sulfate scale precipitated before and after adding the scale inhibitor, through the observation of its appearance, it can be concluded that the crystal form of calcium sulfate scale has changed, and the scale inhibitor will affect the crystal Growth has a hindering effect. The compound product of the new terpolymer (ESA/TPEO/AMPS) and PBTCA has a simple synthesis process, good scale inhibition performance, wide application range, and low price. Among them, the phosphorus and nitrogen content is small, and it is environmentally friendly. Excellent new green environmental protection scale inhibitor

Keywords:Water treatment agent, green environmental protection, dual compound, calcium sulfate resistance

目录

摘 要 I

Abstract II

第一章 绪论 1

1.1选题背景 1

1.1.1引言 1

1.1.2当前阻垢剂的发展与研究 1

1.1.3不同领域复配试剂的优点 1

1.2选题意义 2

1.3课题研究内容及创新点 2

1.3.1研究内容 2

1.3.2创新点 2

第二章 三元聚醚阻垢剂的制备 3

2.1实验仪器和实验试剂 3

2.1.1实验仪器 3

2.1.2实验试剂 3

2.2实验过程 3

2.2.1ESA合成 3

2.2.2TPEO合成 4

2.2.3新型含聚醚三元聚合物合成 4

第三章 复配制剂单组分筛选 5

3.1阻硫酸钙垢检测方法 5

3.2实验仪器和试剂 5

3.2.1实验仪器 5

3.2.2实验试剂 6

3.3复配制剂单组分阻硫酸钙垢性能研究 6

3.3.1自制新型阻垢剂（ESA/TPEO/AMPS） 6

3.3.2 市售（PBTCA和PESA） 9

第四章：复配制剂阻硫酸钙垢性能的研究 11

4.1复配比例对复配制剂阻硫酸钙垢性能的影响 11

4.2 反应时间对复配制剂阻硫酸钙垢性能的影响 11

4.3 反应温度对复配制剂阻硫酸钙垢性能的影响 12

4.4钙离子浓度对复配制剂阻硫酸钙垢性能的影响 13

第五章：复配制剂阻硫酸钙垢机理的研究 15

5.1硫酸钙垢结构机理 15

5.2阻垢剂阻垢机理 15

5.2.1晶格畸变 15

5.2.2螯合增溶作用 15

5.2.3分散与静电斥力作用 15

5.2.4再生—自脱膜机理 15

5.3硫酸钙垢红外测试 15

5.4显微镜分析表征 16

5.5扫描电镜分析表征 18

第六章 结论与展望 19

6.1结论 19

6.2展望 19

致 谢 20

参考文献 21

第一章 绪论

1.1选题背景

剩余内容已隐藏，请支付后下载全文，论文总字数：16212字