论文总字数：12335字

摘 要

水性聚氨酯成膜后具有优异的弹性、耐摩擦和耐低温性，但是它的耐水性和耐化学性较差，为了改善水性聚氨酯的耐水性和耐化学性差的问题，通常将其与聚丙烯酸酯混合，这是因为聚丙烯酸酯具有优异的耐水性和耐化学性，并且价格相对较便宜。

本论文通过使用二羟甲基丙酸(DMPA)、甲基丙烯酸β羟乙酯(HEMA)、聚丙二醇（PPG）、聚乙二醇（PEG）和异佛尔酮二异氰酸酯（IPDI），制备出了一种乙烯基封端型的水性聚氨酯(VLWPU)，同时也制备了用丁二醇（BD）、乙二醇（EG）、乙二胺（EDA）和丙二胺（PDA）等扩链剂扩链的水性聚氨酯,然后用制备的水性聚氨酯作为种子相与合成的聚丙烯酸酯进行混合制得聚氨酯-聚丙烯酸酯复合乳胶膜。论文研究了丁二醇、乙二醇、乙二胺和丙二胺等扩链剂对产品性能的影响，同时研究了PPG和PEG分子量对产品亲水性的影响。

实验结果表明，在PPG与1,4-BD和DMPA总量混合比为1:1是膜性能较好；用PEG合成的膜亲水性明显优于用PPG合成的膜，并且PEG的分子量越大，膜的亲水性能越好；采用二元胺合成的EDA WPU最后乳化得到的乳胶膜亲水性好，扩链剂的柔性链越长，膜的性能越软。

关键字：乙烯基封端型水性聚氨酯 乙二胺扩链型水性聚氨酯 聚氨酯-聚丙烯酸酯复合乳胶膜

ABSTRACT

Waterborne polyurethane film has excellent flexibility, friction resistance and low temperature resistance, but its water resistance and chemical resistance is poor,in order to improve the water resistance of the aqueous polyurethane and solve the problem of poor chemical resistance, we usually mixed it with a polyacrylate, because polyacrylate have excellent water resistance and chemical resistance, and relatively inexpensive.

In this passage, we use dimethylol propionic acid (DMPA) 、 methyl acrylic beta hydroxyl ethyl methacrylate (HEMA)、polypropylene glycol (PPG), polyethylene glycol (PEG) and isophorone diisocyanate (IPDI) to prepare a vinyl terminated type waterborne polyurethane (VLWPU). At the same time, we also prepared a kind of butanediol(BD)、ethylene glycol(EG)、ethylene diamine (EDA)and propylene diamine(PDA) extended chain type waterborne polyurethane (EDAWPU), and then used the prepared Waterborne Polyurethane as seed phase mixed with the synthetic polyacrylate to get the polyurethane-polyacrylate composite latex film.This paper studied the effects of butanediol, ethylene glycol, ethylene diamine and propylene diamine chain extender on the properties of the product, the influence of the molecular weight of PPG and PEG on the hydrophilic product also has been studied.

Experimental results show that the ratio of PPG and the total amount of 1,4-bd and DMPA is 1:1, film performance is good; Hydrophilcity of membrane prepared by PEG is obviously better than the membrane prepared by PPG . PEG molecular weight is greater, better hydrophilic membrane is; EDA WPU membrane synthesied by the diamine finally contributed to a great hydrophilic latex film , the longer the chain extender of flexible chain, properties of the films more soft.

目 录

摘要 I

ABSTRACT II

第一章 文 献 综 述 1

1.1涂料印花粘合剂简介 1

1.2 丙烯酸酯粘合剂 1

1.3 聚氨酯粘合剂 2

1.4. 改性乳液的分类及制备方法 3

1.4.1 共混法 3

1.4.2 互穿聚合物网络聚合法 4

1.4.3 核壳乳液技术 4

第二部分 实验部分 6

2.1 药品 6

2.2 实验步骤 7

2.2.1 乙烯基封端型水性聚氨酯(VL WPU)的合成 7

2.2.2 扩链型水性聚氨酯的合成 8

2.2.3 交联型与未交联型聚氨酯-聚丙烯酸酯复合乳胶的合成 9

2.2.4 物理混合型聚氨酯一聚丙烯酸酯复合乳胶(BPUA)的合成 10

第三部分 结果与讨论 11

3.1 各物质比对膜性能的影响 11

3.2 聚醚对膜亲水性能的影响 11

3.3 扩链剂对膜性能的影响 12

3.4 PA/PU质量比对产品性能的影响 12

第四部分 结论与展望 14

4.1 结论 14

4.2 展望 14

致谢 15

参考文献 16

第一章 文 献 综 述

1.1涂料印花粘合剂简介

织物的涂料印花技术的发展到今天己经有2000多年的历史^[1]了，而且因为它具有一些独特的优点，所以近年来得到了印染行业越来越多的青睐，从而被广泛应用。据统计，全世界范围内，涂料印花织物占印花布总量的比例已经达到了70%以上^[2]，而在美国，涂料印花织物占印花布总产量的比例己经达到80%，涤/棉混纺花布几乎全部采用涂料印花技术^[3]。

涂料印花粘合剂是涂料印花浆的主要组成部成，粘合剂将各种染料或颜料成膜，再使其粘附在织物上，从而达到着色印花的目的。