1. 毕业设计（论文）的内容和要求

具有岩石结构的阳离子无序的钛酸盐正极材料li2mtio4（m = mn、fe、co、ni）由于其极高的理论容量，循环过程中极好的结构稳定性等优点而有望成为新型li离子电池正极材料。

然而，li2mtio4材料的离子扩散速率及电子导电率比较低，影响其电化学性能，一度降低了研究者对此类材料的关注。

课题通过水热反应制备具有纳米结构的阳离子无序的钛酸盐正极材料，比较不同水热反应温度条件下制备的电极材料的微观结构、形貌及电化学性能，在此基础上研究电极材料及表观形貌对电化学性能的影响。

2. 参考文献

1. S.R.S. Prabaharan, M.S. Michael, H. Ikuta, Y. Uchimoto, M. Wakihara, Solid State Ionics 172 (2004) 39#8211;45. 2. L. Sebastian, J. Gopalakrishnan, J. Solid State Chem. 172 (2003) 171#8211;177. 3. M. Kuezma, R. Dominko, D. Hanzˇel, A. Kodre, I. Arcˇon, A. Meden, M. Gaber#353;cˇek, J. Electrochem. Soc. 156 (2009) A809#8211;A816. 4. M. Kuezma, R. Dominko, A. Meden, D. Makovec, M. Bele, J. Jamnik, M. Gaber#353;cˇek, J. Power Sources 189 (2009) 81#8211;88. 5. R. Dominko, C.V.A. Garrido, M. Bele, M. Kuezma, I. Arcon, M. Gaberscek, J. Power Sources 196 (2011) 6856#8211;6862. 6. R. Tr#243;coli, M. Cruz-Yusta, J. Morales, J. Santos-Pe#241;a, Electrochim. Acta 100 (2013) 93#8211;100. 7. Y. Kawano, A. Kitajou, S. Okada, J. Power Sources 242 (2013) 768#8211;774. 8. M. Yang, X.Y. Zhao, Y. Bian, L.M. Ma, Y. Ding, X.D. Shen, J. Mater. Chem. 22 (2012) 6200#8211;6205. 9. S. M. Rezvanizaniani, Z. Liu, Y. Chen and J. Lee: J Power Sources, 2014, 110. 10. C. Wang , L. Wu , H. Wang , W. Zuo , Y. Li and J. Liu: Adv. Funct. Mater., 2015, 25, 3524. 11. B. C. Melot, J-M. Tarascon: Account Chem. Res., 2013, 46, 1226. 12. J. Liu, M. N. Banis, Q. Sun, A. Lushington, R. Li, T. K. Sham and X. Sun: Adv. Mater., 2014, 26, 6472. 13. L. H. Hu, F. Y. Wu, C. T. Lin, A. N. Khlobystov and L. J. Li: Nat. Commun., 2013, 4, 1687. 14. N. R. Khasanova, O. A. Drozhzhin, D. A. Storozhilova, C. Delmas, and E. V. Antipov: Chem. Mater., 2012, 24, 4271. 15. T. N. Ramesh, K. T. Lee, B. L. Ellis and L. F. Nazar: Electrochem. Solid-State Lett., 2010, 13, A43. 16. B. L. Ellis, W. R. M. Makahnouk, Y. Makimura, K. Toghill and L. F. Nazar: Nat. Mater., 2007, 6, 749. 17. T. Ye, P. Barpanda, S. Nishimura, N. Furuta, S. Chung and A. Yamada: Chem. Mater., 2013, 25, 3623. 18. P. Barpanda, M. Ati1, B. C. Melot, G. Rousse, J-N. Chotard, M-L. Doublet, M. T. Sougrati, S. A. Corr, J-C. Jumas and J-M. Tarascon: Nat. Mater., 2011, 10, 772.

3. 毕业设计（论文）进程安排

2017.2.25-2017.3.10：完成文献综述及开题报告的撰写任务、文献翻译完成； 2017.3.11-2017.4.20：完成材料的制备及结构表征； 2017.4.21-2017.5.10：完成电极材料的电化学性能测试； 2017.5.11-2017.6.1：完成实验数据的分析及整理工作，在此基础上完成毕业论文的撰写。

2017.6.2-2017.6.15：修改毕业论文并完成毕业论文的答辩。